Ink type: Polyacrylate-based two-part isocyanate hardener-type.
Usage: Excellent adhesion on various materials, suitable for materials such as processed PP,
coated surface, ABS, PMMA, hard coated PMMA, PC, Processed PET, and aluminum.
Feature: Gloss finish
Widely applicable, demonstrate excellent adhesion to most substrate.
Excellent moisture and solvent resistance.
Halogen-free.
Diluents: Standard solvent: T-926,
Slow dry solvent: T-927
Retarder : T-980
Mixing ratios: Ink: Hardener =100:10
Gel phenomena may occur after 6-8 hours of usage at room temperature after mixing,
leading to Reduced physical performance.
Wash-up :T-31/T-15
Screen mesh : 200-300 mesh / inch polyester or Nylon screens is recommended.
Drying time :Sets to touch-dry in 40 minutes at 25¡æ.
Hard-dries in 1 week(air drying) or 30 minutes at 80¡æ + 2 days air-drying.
When applied to metal substrate, thermal curing for 20 minutes at 120-150¡æ is
required for optimal results.
Notes :When used on electroplated film, dilute with solvent T-900 or T-910 to prevent
solvent attacks to the substrate.(Verification is advised based on substrate differences)
D hardener is extremely sensitive to moisture. Use as soon as possible after opening.
Bubbles and /or pin holes may form based on printing conditions, add 1-2%(by weight )
of care13 as needed.
Add 3-5% of care 73 to enhance adhesion to glass and resistance to boiling and alcohol.
Test conditions:
Ink : HF HSD 120 White /710 Black
Substrate: PC, Aluminum
Drying : 30 minutes at 80¡æ + 1week at room temperature.